Efeitos do condicionamento ácido, do tipo de silano e da ciclagem térmica na resistência ao cisalhamento de braquetes fixados à cerâmica / Effects of acid etching, type of silane and thermocycling on shear bond strength of brackets bonded to ceramic

Esta pesquisa avaliou a resistência de união ao cisalhamento de braquetes metálicos (Rocky Mountain Orthodontics) fixados à cerâmica, variando condicionamento ácido, aplicação do silano e ciclagem térmica. Quanto ao silano, comparou-se o Clearfil Ceramic Primer, que contém um monômero ácido em sua formulação, com o Rely X Ceramic Primer, desprovido do monômero. Foram confeccionados 120 discos em cerâmica IPS Empress Esthetic (Ivoclar) com 8 mm de diâmetro por 5 mm de espessura e separados em oito grupos (n=15): Grupos 1, 2, 5 e 6: ácido fluorídrico a 10% por um minuto; Grupos 1 a 4: silano com monômero ácido; Grupos 5 a 8: silano sem monômero ácido; Grupos 1, 3, 5 e 7: 1.000 ciclos de 5°C e 55°C, 30 segundos cada banho. Em seguida, os braquetes foram fixados à cerâmica com o compósito Transbond XT e fotoativados com luz emitida por diodo (LED – UltraLume 5), com 1100 mW/cm2. As amostras foram estocadas em água destilada a 37°C por 24 horas e submetidas ao teste de resistência ao cisalhamento em uma máquina de ensaio Instron à velocidade de 0,5 mm/min. Os dados foram submetidos à análise de variância e ao teste de Tukey (p < 0,05). Obtiveram significância estatística o aumento da adesividade com o condicionamento ácido e a redução de resistência com a ciclagem térmica. Na comparação entre os silanos, não houve diferença estatisticamente significante. Todos os experimentos atingiram valores de resistência superiores aos estabelecidos para uso clínico.

This study evaluated the shear bond strength of metallic brackets (Rocky Mountain Orthodontics) bonded to ceramic, varying acid etching, silane application, and thermocycling. Concerning silane, Clearfil Ceramic Primer, which contains an acid monomer in its formulation, was compared to Rely X Ceramic Primer, devoid of this monomer. 120 IPS Empress Esthetic (Ivoclar) ceramic disks were made with a diameter of 8 mm and thickness of 5 mm. The specimens were divided into eight groups (n=15): Groups 1, 2, 5, 6: hydrofluoric acid 10% for one minute; Groups 1 to 4: silane with acid monomer; Groups 5 to 8: silane without acid monomer; Groups 1, 3, 5, 7: thermocycled 1,000 times at 5°C and 55°C for 30 seconds. After that, the brackets were bonded to the ceramic with Transbond XT composite and cured with light-emitting diode (LED – Ultralume 5) at 1100 mW/cm². All samples were stored in distilled water at 37°C for 24 hours and submitted to shear bond strength test in an Instron testing machine at a crosshead speed of 0.5 mm/min. The data were submitted both to Anova and Tukey’s Test (p < 0,05). Statistical significance was found both in the adhesiveness increase with the acid etching as well as in the resistance decrease with thermocycling. By comparing the silanes, no statistical significance was found. All the experiments reached shear bond strength values higher than those established for clinical use.

Microinfiltração de diferentes sistemas adesivos na estrutura dental / Microleakage of different adhesive systems in dental structures

O objetivo deste trabalho foi avaliar in vitro a microinfiltração marginal de três sistemas adesivos, sendo Grupo I)sistema convencional de um passo com condicionamento ácido prévio, Grupo II)sistema autocondicionante de dois passos e Grupo III)sistema adesivo autocondicionante de um passo. Foram selecionados 15 pré-molares e confeccionados preparos cavitários ocluso-proximais tipo "slot" nas faces mesiais e distrais e divididos em 3 grupos. Terminadas as restaurações, os espécimes foram submetidos à termociclagem e imersos em azul de metileno a 0,5 por cento. Após sofrerem um corte transversal, as maostras foram fotografadas e avaliado o grau de infiltração marginal. Todos os grupos apresentaram infiltração atingindo pelo menos a junção amelodentinária enquanto o Grupo III mostrou também infiltração dentinária. O teste de Kruskal-Wallis demonstrou que não houve diferença estatística entre os grupos I e II, mas foi significativo em relação ao III. Conclui-se que nenhum dos três sistemas estudados foi capaz de evitar totalmente a microinfiltração.

Estudo in vitro da eficácia de um gel EDTA na remoção da "smear layer" da superfície radicular / In vitro study of the efficacy of an EDTA gel to remove root surface smear layer

O objetivo deste estudo foi avaliar a influência da concentração, do tempo e do modo de aplicação de um gel de EDTA na eficácia de remoção de "smear layer" da superfície radicular. Dentes humanos extraídos por diferentes razões foram submetidos à remoção do cemento com fresa diamantada e ao alisamento radicular com cureta. As amostras obtidas receberam aleatoriamente a aplicação de gel de EDTA nas concentrações de 5%, 10%, 15%, 20% e 24%. Para cada grupo experimental, os tempos de aplicação foram de 1, 2 e 3 minutos. Quanto à forma de aplicação, os produtos testados foram aplicados de maneira passiva ou ativa (esfregação com pincel). A seguir, as amostras foram desidratadas e metalizadas para a obtenção de fotomicrografias em microscópio eletrônico de varredura, as quais foram avaliadas, adotando-se o índice de remoção da "smear layer" proposto por Sampaio (1999). Os resultados demonstraram maior remoção da "smear layer" nos grupos tratados com gel de EDTA em relação ao grupo controle. O gel de EDTA a 5% proporcionou remoção mais efetiva da "smear layer" do que as demais concentrações avaliadas, quando aplicados de maneira passiva. Não houve diferenças estatisticamente significativas entre as concentrações avaliadas, quando aplicados ativamente. O tempo de aplicação de 3 minutos, de maneira contínua ou através de lavagem e reaplicação, mostrou-se superior ao tempo de 1 minuto. A aplicação ativa mostrou-se superior à aplicação passiva, exceto para o gel de EDTA a 5%. Pode-se concluir que o tratamento químico da superfície radicular com gel de EDTA de maneira ativa durante 3 minutos pode favorecer a remoção da "smear layer" produzida durante a raspagem e o alisamento radicular

in vitro study on the effect of degree of convergence angles and different surface treatments on retention of resin bonded full coverage prostheses

This study was directed to evaluate the effect of different degrees of convergence angle [10°, 15°, 20° or 25°] and different types of surface treatments of alloy [Sandblasting with 250 microns] [A1203], tin-electroplating and 9.6% hydrofluoric acid etching] on retention of resin bonded full coverage restorations. A total of sixty sound molar teeth were retained in self-cure acrylic resin blocks and divided into four main groups of 15 each. Each group was subjected to preparation with convergence angle [10°, 15°, 20° or 25°]. The four main groups were sub-divided into three sub groups of 5 each. The restorations of each one of these subgroups was subjected to sandblasting with 250 microns [A1[2]O[3]], tin electroplating or 9.6% hydrofluoric acid etching. All samples after treatment were cemented to its prepared tooth using adhesive resin cement and subjected to tensile test using Lloyd testing machine. The failure load was recorded in kilograms. From the results it was found that, elevation of convergence angle of the prepared tooth surfaces reduced the retentive strength of resin bonded full coverage restorations. Sandblasting using 250 microns [A1[2]O[3] produced a superior bond strength compared with tin electroplating and 9.6% hydrofluoric acid etching

Influência do colágeno na resistência de uniäo à dentina úmida e seca / Influence of collagen on the tensile bond strength to wet and dry dentin

O propósito deste estudo foi avaliar se a remoçäo do colágeno exposto pelo condicionamento ácido afeta a resistência de uniäo à dentina em substrato úmido e em seco. Quarenta molares hígidos foram incluídos em resina epóxica e lixados até a obtençäo de uma superfície plana. A área de adesäo foi delimitada em 3 mm e os dentes foram divididos aleatoriamente em 4 grupos. No grupo 1, o adesivo (Single Bond, 3M) foi aplicado segundo as recomendaçöes do fabricante, deixando-se uma superfície úmida. Grupo 2: após condicionamento ácido e lavagem, secou-se a dentina com jato de ar (20 s) e aplicou-se o adesivo. Grupo 3: após condicionamento ácido e lavagem, a dentina foi tratado com NaOCl a 10 por cento (60 s) e lavada (15 s). A superfície dentinária foi levemente seca com papel absorvente, deixando-se uma superfície úmida. Grupo 4: procedeu-se da mesma forma que no grupo anterior, porém, após a desproteinizaçäo com NaOCl, realizou-se uma secagem com jato de ar por 20 s antes da aplicaçäo do adesivo. A seguir, confeccionou-se um cone de resina (Z100, 3M) com uma matriz de Teflon. Os espécimes foram submetidos ao teste de traçäo (Mini Instron) e os resultados em MPa (ñSD) foram: grupo 1: 13,85 ñ 3,37; grupo 2: 8,87 ñ 3,31; grupo 3: 12,24 ñ 1,07; grupo 4: 11,85 ñ 1,73. A análise de variância e o teste de Tukey demonstraram que os grupos 1, 3 e 4 tiveram forças de adesäo semelhantes e maiores que a do grupo 2 (p < 0,001). Baseado nos resultados, é lícito concluir que o tratamento com hipoclorito de sódio näo altera a resistência adesiva para o adesivo em estudo, tornando-o insensível à condiçäo do substrato (úmido ou seco). No entanto, quando o colágeno é mantido, deve-se realizar a técnica de adesäo úmida

A problemática do condicionamento ácido do tecido dentinário / Questioning the dentin acid-etching

Este trabalho de revisäo bibliográfica, teve por objetivo esclarecer quais os efeitos do condicionamento ácido no tecido dentinário, visando estabelecer parâmetros para a escolha do melhor tratamento da dentina no momento da restauraçäo

Avaliaçäo clínica e histopatológica da polpa dental de humanos jovens 60 dias após seu condicionamento com ácido fosfórico a 37 por cento e colocaçäo de um sistema adesivo de quarta geraçäo sobre a área da exposiçäo / The clinical and histopathologic evaluation of the young human dental pulp 60 days after 37 per cent phosphoric acid action's and phacement of on adhesive system of the fourth generation in an exposition area

Neste trabalho, os autores observaram a açäo do ácido fosfórico a 37 por cento de um sistema adesivo em contato íntimo com a polpa de humanos jovens. Análise clínica e histopatológica, 60 dias após, constatou-se ausência de infiltraçäo com discreta fibrose na área de exposiçäo

Análise comparativa, ao microscópio eletrônico de varredura, de esmalte bovino exposto a diferentes soluçöes ácidas: um estudo in vitro / Scanning electron microscopy analysis of bovine enamel exposed to different acid solutions: an in vitro study

O presente estudo teve por objetivo analisar as possíveis alteraçöes ocorridas na superfície de esmalte bovino, hígido ou desmineralizado, exposto por 40 minutos à Coca-cola em fórmula original, ao suco de limäo diluído em água destilada na razäo 1:5 e ao suco de laranja natural integral (Parmalat). Com esse fim, 40 blocos de esmalte bovino de 16 mm² foram previamente limpos com pedra-pomes e água destilada, em baixa rotaçäo. Desse total, 20 foram artificialmente descalcificados. Tanto os blocos hígidos quando os descalcificados foram colocados 6 a 6 em dispositivos de cera, perfazendo um total de 3 dispositivos com 6 blocos de esmalte hígido (Grupo I) e 3 dispositivos com 6 blocos de esmalte descalcificado (Grupo II). Análises comparativas ao Microscópio Eletrônico de Varredura demonstraram que o suco de limäo foi o responsável por padröes de erosäo mais acentuados, seguido pela Coca-cola e pelo suco de laranja, tanto no esmalte hígido quanto no desmineralizado. Os resultados evidenciam o potencial erosivo do suco de limäo, da Coca-cola e do suco de laranja

Efeitos da fonte de calor e do tratamento térmico sobre a dureza superficial e a resistência à corrosäo de ligas metálicas alternativas para uso odontológico / Effects of casting sources and heat treatment on hardness and corrosion resistance of dental base metal alloys

Estudou-se a dureza superficial e a resistência à corrosäo de cinco ligas metálicas alternativas para uso odontológico, fundidas por duas diferentes fontes de calor e sofrendo três diferentes tipos de tratamentos térmicos. Concluiu-se que a liga P (experimental) apresentou os maiores resultados de dureza superficial e os menores resultados de corrosäo superficial. Também foi a liga P (experimental) a única sensível aos tratamentos térmicos e às fontes de calor utilizadas